Category Archives: Die Casting

 

Aluminium is an exceptional material because of its many advantages. It is prevalent in the construction, infrastructure and transport sectors due to its long life, low maintenance and contribution to energy efficiency, to name a few!

DURABLE

Aluminium is highly resistant to corrosion and can be used for low-maintenance structures. However, selecting the correct alloys and joining methods is vital to ensure maximum durability.

CORROSION RESISTANT

Aluminium Die Casting

A solid oxide layer is naturally created on the surface of aluminium when it comes into contact with air. This natural passivation acts as a barrier between the atmosphere and the aluminium, which protects aluminium alloys from corrosion.

MALLEABLE

Aluminium is easy to work with metal. Its relatively low melting temperature makes it advantageous for foundry operations. In addition, aluminium is a ductile metal. This makes it an easy metal to roll, forge, extrude and for all other plastic deformation processes. The material can be cut into three-dimensional shapes, formed, welded, screwed, etc. In addition, extrusions can be custom-made to the designer’s design at a reasonable cost or purchased from distributors who maintain inventories of standard extruded profiles.

Like rolling, cold forming improves the mechanical characteristics of aluminium and offers a high-quality surface finish.

RECYCLABLE

Aluminium Die Casting

Aluminium is fully and infinitely recyclable, making it environmentally friendly. Its life cycle is an infinite loop. In addition, recycling aluminium is relatively simple and requires only 5% of the energy of the actual electrolysis production process. It is estimated that 75% of the aluminium produced since the discovery of the electrolysis process is still in circulation and reused or recycled.

LIGHTWEIGHT

Aluminium Die Casting

Aluminium is a preferred alternative for reducing the mass of structures. Aluminium allows for a lower tare load, which increases the payload, a significant advantage in the transport market. The density of aluminium is about three times less than that of steel. It is possible to have aluminium alloys with a similar yield and ultimate strength to commercial steels. It should be noted, however, that the modulus of elasticity of aluminium is also three times smaller than steel’s, hence the need to consider all properties when designing a structure.

ECONOMICAL

Aluminium Die Casting

Aluminium requires little maintenance, which translates into lower maintenance costs in the long term. No preventive measures are needed to preserve its characteristics. In short, aluminium requires minimal investment and has a maximum economic and social impact.

Compared to steel, the price per kilogram of aluminium is higher. On the other hand, the optimisation of aluminium profiles obtained by extrusion allows for shapes that, in some cases, can withstand similar forces while being lighter. The lighter structures result in lower labour costs for the project assembly. An aluminium extrusion can be unpainted and modular.

In addition, you should consider the total cost of ownership as aluminium is more advantageous in the long term. It requires less maintenance, and you can sell it for much more than steel at the end of its life.

In an interview in Aluminium 101 magazine, Benoît Comeau of Panfab Industries says they can offer aluminium panels at the same price as steel panels. Michel Guillot, a professor at Laval University, says that people overestimate the cost by wanting to do in aluminium what they do in steel. Jean Simard of the Aluminium Association of Canada says that we need to design with the characteristics of aluminium and not use it as a substitute for steel.

CONDUCTIVITY

Aluminium Die Casting

Aluminium is a good conductor of both electricity and heat. Aluminium is a high-voltage electrical wire because of its conductivity-to-density ratio. It is also ubiquitous to use aluminium in heat transfer systems such as air conditioning heat exchangers, automotive radiators, etc.

MECHANICAL STRENGTH

Aluminium Die Casting

Aluminium is adapted to the application and the forming process. By using aluminium in alloy form, an increase in strength is obtained, making aluminium suitable for structural applications. For some alloys, it can be increased by cold working. Generally, if an extruded profile is required, such as mullions used in curtain wall design, the more extrudable 6000 series alloys will be used. In facades, the aluminium cladding is designed from sheet metal.

Therefore, if you are looking for Aluminium Die Casting, Gravity Die Casting, Low-Pressure Die Casting, Sand Casting, and Casting Porosity Sealing & Impregnation for the particular purpose of your business, Alliance Connect can help you out. They are accredited to ISO9001 quality standards, which cover national and international markets, serving a broad range of industries, including automotive, industrial, mining, government, defence, marine, municipalities and the arts.

 

Die casting is an industrial manufacturing process that uses tooling to produce metal parts. When these parts have a complex and precise geometric shape, no other industrial process can achieve the result that die casting gives. This process uses molten alloy or metal injected into a high-pressure chamber. So, without further ado, let’s dive into this blog and learn some of the advantages of die casting.

Die casting process

die

In this process, reusable steel molds are preheated and possibly coated with a release agent to protect the tool surfaces and lubricate them before each use. The molten metals are pre-measured and injected at very high pressure into these molds. The selected alloy is fed to the mold cavities through the gooseneck, the machine nozzle, and the feed channels. The part is ejected from the mold.

The plunger returns to its upper position, the gooseneck opening is released, and the injection chamber is automatically filled with molten metal. The machine is then ready for the next injection. This high-pressure process gives the parts a dense, fine-grained surface structure with a wide range of physical and mechanical properties, such as fatigue strength, which is an important criterion for metal selection.

Indeed, fatigue failure is the most common occurrence in mechanical parts. It has a fatigue strength seven to ten times greater than ABS-type plastic. The choice of metals or alloys to be used also depends on the specifications and function of the part. One of the most commonly used processes in aluminum die casting. Other metals, such as brass, magnesium, and zinc alloys, are also used.

What are the advantages of die casting?

1. Perfect for fast and high-volume production

This casting process allows for high production rates. The process can be repeated hundreds of thousands of times with hardened steel injection molds to create perfectly identical metal parts. With zinc alloys, production rates on conventional hot-chamber machines are high and can, in some cases, exceed a thousand injections per hour for thin, small parts. Die casting is therefore ideally suited for high-volume production. Moreover, it requires little or no machining.

2. Durable and accurate molds

The tools are strong and long-lasting. They are also heat resistant, have good dimensional stability, and maintain close tolerances. Depending on the complexity of the part, the high precision of the tools allows the elimination of a maximum of machining operations. With tooling, life is longer, which helps to reduce production costs.

3. Durable parts

die

Die-cast parts, even those with very thin walls, are stronger than their plastic counterparts of exactly the same shape or size. In addition, they are stronger because these functional parts can be molded as a single unit, eliminating the need for the assembly of different parts.

4. Finishing

Several finishing processes can be applied to the raw castings. Firstly, for the preparation of the surfaces, there is shot blasting, which is a projection of metallic particles on the parts in order to remove the burrs and traces of molding. Then there is sandblasting, which is the projection of sand or small glass beads on the part using a directed jet.

Tribofinishing: the parts are placed in a vibrating tank that contains abrasive ceramic pebbles. Grinding and deburring allow for manual removal of marks, usually on large and/or small parts, and finally, there is polishing, which is done prior to a very high-quality surface treatment, allowing preparation for bright chrome or beautiful gold plating.

5. Assembly

To eliminate machining operations (drilling, threading, and tapping) and assembly elements (screws, nuts, rivets), die-casting gives the possibility to realize connections such as crimping, riveting, screwing, press-fitting, gluing, or overmolded insert. It is perfectly suited for these types of connections.

Looking for help?

die

Are you looking for a professional die casting company? Are you in Montreal? Then look no further than Capitol Industries, Inc. They are a renowned cam and specialty locks manufacturer. The company’s factory in Montreal, Canada, provides customers with a full range of services, including quotation, tooling design, production, process design, manufacturing, and finishing.

Their products include locksmith, cam locks, specialty locks, cabinet locks, master keyed locks, mailbox locks, letterbox locks, and more. For more information, please visit the company’s website. So, what are you waiting for? Give them a call and make all your dreams become a reality with the help of their team of experts.

Topics covered:

 – 1. Introduction

 – 2. Components of a mould and the production cell 3

 – 3. Traditional Die Casting

 – 4. Vacuum die casting

 – 5. Alloys for die casting

 – 6. Semi-solid die casting

 – 7. Die Casting in Australia

1. Introduction

 The low melting point of aluminium makes it possible to use a permanent steel mould for castings. An injection plunger pushes liquid aluminium into the mould cavity and compresses the part during solidification in die casting. During solidification, the liquid metal typically reaches speeds of up to 60 meters per second, with pressures reaching 800 bar. The clamping force employed by the moulding press to hold the cavity closed and the pressure provided by the plunger to contain the pressure exerted on the part are defined by the size of the cavity and the pressure supplied by the plunger to hold the pressure exerted on the part. Most miniature presses have a capacity of 1000 kN and the most extensive 35000 kN (3500 T). Therefore, the force of the press is directly related to the projected surface of the moulded part.

 The die casting process is divided into 6 phases: liquid metal transfer, injection approach phase, rapid injection, intensification, ejection and mould lubrication. Each stage is optimized to maximize the production rate and minimize the number of rejected parts.

 There are three variants of this process:

 – Traditional die casting

 – Vacuum die casting, including vacuum casting for structural applications

 – Semi-solid die casting, which is much less common.

 The main advantage of this process is the fast production rate, which lowers production costs and approaches mass markets such as automotive. The metal mould’s quick cooling results in an excellent metallurgical structure on the skin’s surface, contributing to good mechanical qualities. The surface polish is outstanding, as are the dimensional tolerances. The design freedom, on the other hand, is limited to the mould opening axis. The process is low labour-intensive but has high capital and tooling cost. For a large production run of more than 10,000 parts, the die casting process offers the lowest production cost per part among the foundry processes.

 The main disadvantage of the traditional process (where no vacuum is applied in the cavity) is porosity in the centre of the die-cast parts due to air trapped during the injection. When the part is heated, the entrapped air causes blisters to form. These blisters are created by the gas trapped in part expanding, making it impossible to execute typical solution heat treatments to achieve optimal mechanical qualities; this phenomenon also makes welding and the application of some baked paints difficult. Because the casting skin offers mechanical strength, many classic die castings can still be effectively cast, accounting for more than half of all aluminium castings produced.

In conventional die casting, secondary alloys (recycled) with a high alloying element content (iron and zinc) are often used, which gives good mechanical strength despite an elongation of less than 3%. Heat treatment is used to improve the mechanical strength of die-cast alloys while preventing blisters.

Using a vacuum in the cavity to reduce trapped air and real-time management of the casting cycle results in exceptional component quality. Maximum elongation at break is achieved by combining a high vacuum pressure method (50 bar) with low iron primary alloy formation. It allows parts used in structural applications to be heat treated. The desire to lower the weight of land vehicles is driving these innovations, and vacuum die casting is the appropriate choice for a high-speed casting technique for structural aluminium castings. The most active area in the foundry field is the development of this method and dedicated alloys.

2. Elements of a mould and the production cell

The die casting process has two principles of feeding the liquid metal: hot chamber technology and cold chamber technology. The hot chamber process uses a plunger directly into the molten metal bath to feed the mould. In contrast, the freezing chamber process uses a “cold” container into which the liquid metal required to fill the part is transferred by a ladle (spoon) or by a dosing robot. Since the aluminium dissolves the steel, aluminium die-cast parts are produced only in a cold room.

2.1 Description of the die casting mould

The die casting mould consists, in most cases, of two metal shells made of ferrous alloys. Depending on the number of parts planned, the materials used to manufacture the shells are :

– H13 type tool steel for the cavities

– 4140 alloy steel or P20 tool steel for the support parts

The ejector rods are always made of a more rigid material, and in some cases, they are surface treated (e.g. by nitriding) to limit aluminium sticking.

The mould consists of a fixed part on the liquid metal supply side and a movable part on the other. The fixed part contains the metal inlet hole and part of the part cavity. It can also have cores (fixed or sliding) to mould cavities in part. The movable part contains the ejector pins used for demoulding in addition to the cores and the part cavity. The moulds are equipped with oil (heated) or water cooling channels that also serve to preheat the mould at the start in hot oil.

 The primary insert is frequently housed in a more oversized, permanent frame that can create multiple types of parts to save money on tooling. The customer usually owns the inserts or moulds.

Thin walls of up to 1.5 mm are well suited to the technique. It is best to use invariant sections that solidify simultaneously. There are no feeders, and the cuts on the parts are small to facilitate cutting on deburring presses after casting. The part design makes extensive use of ribs to increase rigidity and strength, which also helps to fill the cavity quickly before the alloy solidifies and vent the gases. Metal turbulence in the cavity is controlled by the metal injection rate, the size and positioning of the feed channels and gates, the shape of the cavity (primarily ribs), and the use of washout stubs (small gaps added to the end of the moulding) that serve to balance metal movement and capture inclusions formed during filling. In the case of sous vide, the vacuum application parameters are also important for filling.

2.2 Description of the Die Casting Press

Aluminium Die Casting

The moulding machine consists of three central units: the injection unit, the closing unit and the peripherals (pouring robot, lubrication arm, air draft system). A hydraulic motor drives the whole machine.

An injection accumulator, an injection cylinder, a multiplying accumulator, a multiplying cylinder, and an injection cylinder positioning cylinder make up the injection unit, which is a sophisticated hydraulic system. These components allow to modulate the speed of the injection piston in 3 phases to obtain a slow pace for the approach (phase 1 of the filling), a fast acceleration thanks to the injection accumulator during the filling (phase 2) and the compaction of the metal with the help of the multiplier accumulator during the intensification (phase 3). Modern systems allow for exact control of the speed curve and a gradual transition from approach to full speed. In contrast, earlier systems are sometimes limited to a single operation.

The clamping unit consists of a movable plate that contains the ejection system and a fixed plate where the coupling with the injection unit is located. A clamping system consisting of toggle levers is used to apply the clamping force to the machine plates. During the intensification process, this clamping force must be greater than the metal’s force. The pressure exerted by the metal is calculated according to the following formula:

F= Pint * A

where F is the metal force, Pint is the intensification pressure, and A is the part’s projected area, including the cookie and the runners/washers.

Typically, the closing force should be at least 20% higher than the opening force exerted by the metal. The press is built with a solid frame and the alignment of the moving and fixed platens. These columns are placed in tension by the clamping system and must be well balanced to promote a uniform application of the clamping force.

The press is equipped with :

  • peripheral connections for the mould, cylinder and piston temperature control system, 
  • liquid metal dosing system, 
  • automatic mould lubrication system, 
  • air supply system, 
  • operating interfaces and the safety elements.

The machine can also contain or be connected to data acquisition and a real-time control system for the injection cycle. Fast-response sensors measure the pressure and position of the injection plunger almost instantaneously, with feedback to keep the parameters within pre-set ranges. The information can be recorded or viewed offline or remotely and used for statistical quality control.

Lubricant is used to facilitate the demoulding and cooling of the mould. However, because of the increased availability of simulation software that allows for more precise design of the mould temperature management, lubricant savings, and cycle time optimization, this method is becoming less common. The lubricant applied to the mould between injections is 100% liquid and does not contain any ceramic suspension as in permanent moulds; Dimensional tolerances are unaffected. It is either manually applied or, more commonly, automatically applied.

The thermoregulation system consists of a mould heater with a heat transfer fluid that cools the mould. It can also be connected to a sophisticated temperature acquisition system on the mould for closed-loop control. The cell can contain a water tank to soak the parts after casting and a deburring press to cut the feeding system to the attacks. The manufacturing cell can be fully automated, from loading the holding furnace to installing the insert and applying lubrication to the etch cut.

In the case of the vacuum process, there is a vacuum pump and vacuum tank nearby.

2.3 Tooling design

The caster is responsible for the design of the mould, which includes the following features:

– Addition of foundry shrinkage, as the liquid aluminium contracts during solidification and in the solid-state. The intensification pressure usually compensates for the contraction of the liquid before solidification.

– Addition of draft angles that allow the part to be ejected.

– Design of the feeding system was calculated to fill the cavity with the minimum of turbulence before solidification starts.

– Design of the ejection system.

– Design of drawer cores for complex cavities.

Filling and solidification modelling is widely used in die casting design due to the high cost of tooling modifications.

A foundry-appropriate part design from the start increases the degree of success in bringing a die-cast part to production. In general, you should:

– Use uniform thin sections

– Avoid isolated metal masses away from the feed channels

– Use radii and limit sharp corners

– Use ribs instead of solid walls

– Take into account the (almost unique) demoulding axis and the associated loss of design freedom

– Consider the associated above and below mould tolerances that are not moulded together

– Anticipate that the moulding will have draft angles and be marked by ejector pins.

2.4 Die Casting Benefits and Capabilities

Die casting offers the best dimensional tolerances of any casting process. Fine details and small cavities can be moulded as well as fine identification lettering. Die casting is characterized by moulding thin-walled parts up to 1.5 mm, surrounded by reinforcing ribs. The surface finish is excellent, and 60 microinches RMS is easily achieved, but 90 microinches RMS is more conservative. Structural parts can be made due to the fine structure caused by rapid cooling, vacuum, and low iron primary alloys. Inserts can also be installed in the mould to change the appearance of the moulding, such as steel.

The technique has several environmental benefits, including the elimination of sand moulds, the ability to use recycled alloys for commercial parts, and the need for minimal post-casting polishing.

Because of the metal’s high pressure, sand cores are not an option. If a metal core (spool) is used in another axis, it must resist the metal’s push, necessitating a more powerful hydraulic system. Consequently, we avoid using cores or a core ejected with the part and removed after the casting. Note the use of salt core for complex cavities, which is then removed by cleaning with water.

2.5 Die Casting Markets

In summary, the process offers the following characteristics:

– Minimal cost for large production runs

– Excellent dimensional tolerances and surface finish

– Minimum machining required after casting

– Parts with limited design freedom in 2 axes

– Wide choice of alloys available

The traditional die casting market is focused on mass-produced parts, small hardware industry, fasteners, housings (covers), automotive parts (valve covers, wiper arm supports, housings, small engine blocks).

Vacuum processes with structural alloys and semi-solid casting allow structural parts for the automotive market (engine cradles, A and B pillars, door structures, connecting parts).

3. Traditional die casting

This moulding technique enables the mass manufacture of commercial products in enormous quantities. A sound and dense surface layer provide mechanical strength. On the other hand, elongations at break are low, and the centre of the component is usually porous.

The piston moves fast, reaching a maximum of 2.12 m/s in the last few centimetres of its stroke before slowing down. The metal’s pressure (white line) rises to 260 bar. The yellow curve on the right depicts the position of the piston at the end of the injection during the intensification phase.

4. Vacuum pressure moulding

During the moulding cycle, a vacuum of between 25 kPa and 7 kPa is used to evacuate the air in the cavity. This is a method for reducing porosity and obtaining a dense portion by reducing the presence of porosity. Vacuum in conjunction with heat treatable, low iron alloys that will maintain good elongation at break is necessary for structural applications. A vacuum pump and vacuum tank achieve the vacuum. At the start of the injection cycle, a vacuum is created in the cavity, maintained until the final filling. The vacuum is started by the central machine controller utilizing a valve on the mould or, more simply, a vast air draw and an opening valve. The mould must also feature a mechanical valve system or a cooling block with a baffle to prevent liquid metal from entering the air draft system (solid air draft). The size of the press determines whether a mechanical valve or a cooling block system is used. Valves have a smaller projected area, but they are more expensive and difficult to maintain. The vacuum level obtained in the mould cavity is also affected by the choice of the blocking system of the air duct; the valves having a faster response allow reaching an adequate level of a vacuum more quickly.

Vacuum moulding of automotive structural parts has seen significant technological advancement. The following methods are employed:

– The use of low-iron alloys with magnesium for heat treatments and strontium for structural modification.

– Turbulence-free container filling using a scupper or by tilting the furnace with in-line liquid metal filtration.

– Use of vacuum die casting.

– Process control and mould temperature control.

– Development of heat treatments.

5. Alloys for die casting

Traditional die casting alloys include 380, made from recycled aluminium, and 383, which is more fluid for fine detail casting. 360 is another standard alloy, which is employed in high-strength applications for intricate and corrosion-prone parts. Low iron content alloys (A380 and A360) are also available for more excellent elongation at break. Still, their use reduces tool life due to the attack of the mould by liquid aluminium.

Other common alloys are:

– 413 used for more excellent wear resistance and for sealing parts

– 443 for good ductility

– 390 for engine blocks

– 518 for marine parts

These alloys are also used for vacuum casting when we want to limit the porosity in the parts.

The vacuum die casting process allows the use of a new range of alloys for structural applications. These alloys (Table 2) contain silicon in the range of 7-12%, iron content generally less than 0.25%, and magnesium for good flowability and heat treatability. They also contain manganese and strontium to limit sticking in the mould. These alloys provide yield strengths of 100 to 230 MPa with elongations of 4 to 20% in the F and T5 T6 and T7 heat-treated states.

6. Semi-solid pressure casting

Since the late 1990s, these methods have been applied in industry. The goal is to use a mould to cast an alloy in the paste phase (50 per cent solid). This enables you to obtain:

– The decrease in porosity

– Tighter tolerances on dimensions

– Less mould wear – High manufacturing rate – Improved mechanical properties

Apart from the low porosity of the castings, a “rounding” of the metallurgical structure during the paste manufacturing process improves mechanical qualities (particularly elongation). The spherical form of the paste allows the rheofluidization of the flow during casting, i.e. the flow becomes easier as the speed increases. Turbulence and flow separation are eliminated in this type of flow, and in addition, the air in the cavity is evacuated ahead of the flow front. This results in the production of healthy parts.

New rheo-casting UBE

– Slurry on-demand HanJoo SoD

– Semi-solid rheocasting Bhuler

– Sub liquidus casting from THT presses (vertical casting process)

– Swirled enthalpy equilibration device SEED STAS

– Continuous the conversion process CRP MPI/WPI

These processes combine various stirring methods during the solidification phase and loading the paste into the press container.

7. Die Casting in Australia

Alliance Connect manufactures a comprehensive range of high-quality aluminium die casting alloys for a variety of applications. They’ve been providing exceptional metal products to all of Australia for over 60 years.